Madras Fertilizers Limited has published Tender For Procurement Of Fused Alumina Lumps / Honey Comb Tiles / Electro Fused Bricks / Ceramic Balls. Submission Date for this Tender is 27-10-2023. Chemical Supply Tenders in manali Tamil Nadu. Bidders can get complete Tender details and download the document.
Sl. No. | Item Description |
1 | CERAMIC BALLS- SIZE 1/2" SPECIFICATION: CHEMICAL ANALYSIS: Al2O3, % :: 23 - 26 SiO2,% :: 63 - 72 Fe2O3+TiO2, % ::APPROX. 2.5 MgO _ CaO,% ::APPROX. 0.55 Na2O + K2O,%::APPROX. 2.3 SOLUBLE IRON ACCORDING TO ASTM-C 279 SHOULD BE APPROX.0.005% PHYSICAL VALUES: SPECIFIC GRAVITY, g/cm3 : 2.4 HARDNESS (Mohs SCALE) : 8 TENSILE STRENGTH, N/mm2 : 45 COMPRESSIVE STRENGTH, N/mm2 : 400 COEFFICIENT OF EXPANSION: 1/DEG.CENT :: 4.7 X 10 6 THERMAL CONDUCTIVITY: kJ/M, H, DEG.CENT -6.3 SPECIFIC HEAT, kJ/KG, DEG.CENT :0.84 MAX. APPLICATION TEMP, DEG.CENT:1,200 MODULUS OF ELASTICITY, N/mm2 :60,000 WATER ABSORPTION,% ::0.1 - 3 OPERATING CONDITIONS: TEMP. DEG. CENT, MAX.:: 450 PRESSURE, KG/CM2 G, MAX, ::50 GAS COMPOSITION: CONTAINING SULPHUROUS COMPOUNDS AND PROCESS GAS WITH VARIOUS CONTENTS OF CO, CO2, H2, CH4, N2, Ar, AND STEAM |
2 | ELECTRO FUSED ALUMINA LUMPS FOR SECONDARY REFORMER SIZE:50-100MM MATERIAL: HIGH PURITY ELECTROFUSED ALUMINIUM OXIDE HAVING A QUALITY AS "CHRISTALBA" FROM SOCIETY FRANCAISE "D" ELECTRO MATALLURGIE OR EQUIVALENT COMPOSITION AL2O3 - 99.4 WT% NA2O+K2O-0.15-0.5 WT% FE2O3-0.10-0.5 WT% SIO2-0.02 WT% TIO2 - TRACES V2O5 - TRACES BULK DENSITY:2G/CM2 |
3 | ELECTRO FUSED ALUMINA LUMPS FOR SECONDARY REFORMER SIZE:100-200MM MATERIAL: HIGH PURITY ELECTROFUSED ALUMINIUM OXIDE HAVING A QUALITY AS " CHRISTALBA" FROM SOCIETY FRANCAISE "D" ELECTRO MATALLURGIE OR EQUIVALENT COMPOSITION AL2O3 - 99.4 WT% NA2O+K2O-0.15 - 0.5WT% FE2O3 - 0.10 - 0.5 WT% SIO2 - 0.02 WT% TIO2 - TRACES V2O5 - TRACES BULK DENSITY - 2G/CM3 |
4 | ELECTROFUSED ALUMINA LUMPS FOR SECONDARY REFORMER SIZE 25-50 MM MATERIAL:HIGH PURITY ELECTROFUSED ALUMINIUM OXIDE HAVING A UALITY AS "CHRISTALBA" FROM SOCIETY FRANCAISE "D" ELECTRO MATALLURGIE OR EQUIVALENT COMPOSITION: Al2O3 -99.4WT% nA2O K2O - 0.15 - 0.5WT% Fe2O3- 0.10 - 0.5 WT% Si2O3 - 0.02 WT% TiO2-Traces V2O3-Traces BULK DENSITY - 2G/CM3 |
5 | ELECTROFUSED UNIVERSAL CIRCLE BRICK FOR SECONDARY REFORMER TOP CATALYST BED |
6 | HONEYCOMB TILES FOR SECONDARY REFORMER CATALYST BED TOP - TILES WITH 19 HOLES MATERIAL : HIGH ALUMINA FIRE BRICK DIMENSION AS PER HALDOR TOPSOE DRAWING COMPOSITION OF ALUMINA TILES: SiO2 <0.06% Fe2O3<0.15% ALKALIES <0.3% Cl <50PPM S<50PPM As <50PPM PARTICLE DENSITY :3.25 G/CM3 APPAENT POROSITY 15-18% |
7 | HONEYCOMB TILES FOR SECONDARY REFORMER CATALYST BED TOP : MATERIAL: HIGH ALUMINA FIRE BRICK TILES WITHOUT HOLES (DUMMY TILES) DIMENSION OF THE TILES GIVEN IN HALDOR TOPSOE DRAWING COMPOSITION OF ALUMINA TILES: SiO2<0.06% Fe2O3 <0.15% ALKALIES<0.3% C1<50 PPM S <50 PPM As<50 PPM PARTICLE DENSITY :3.25 G/CM3 APPARENT POROSITY :15 - 18% |