Tender For Supply Of Plastic Refractory And Super Castable Refractory, parichha-Uttar Pradesh

Supply Of Plastic Refractory And Super Castable Refractory , Refractory Supercastable Alumina 68-72%, Super Castable Refractoryas Per Following Specification:Al2o3:68-72%, Cao:5.2-6%, Fe2o3:4.8-5.5%, Max Service Temp:1450 °C, Max Grain Size:5Mm, Water Required For Casting:10-11%, Dry Density:2.50-2.65 G / Cc, ( After Drying At 110 °C / 24 Hrs ) , Ccs:350-450 Kg / Cm2 ( After Drying At 110 °C / 24 Hrs ) Refractoriness, Orton / °C Plc, % ( After Heating At 1100 Deg C / 3Hrs:-0.30 To +0.30 ) After Heating At 1400 Deg C / 3 Hrs:-1.60 To +1.70 ) , Refractory Plastic Alumina 82.5-85.5, Plastic Refractory As Per Following Specification:Al2o3:82.5-85.5%, Fe2o3:0.50-0.85, Max Service Temp:1700 °C, Max Grain Size:3Mm, Pre-8 Liquid For Ramming:9.7-10.7%, Dry Density :2.70-2.85 G / Cc, ( After Drying At 110 °C / 24 Hrs ) , Ccs:260-430 Kg / Cm2 ( After Drying At 110 °C / 24 Hrs ) Refractoriness, Orton / °C Plc, % ( After Heating At 550°C / 3Hrs:-0.3 To +0.3 ) After Heating At 815 °C / 3 Hrs: -0.3 To +0.3 ) , Refractory Supercastable Alumina 68-72%, Fire Crete Super Castable Refractory ( Type -70% Al Castable, Nature Of Bond #Castable Insulation ) , Refractory Supercastable Alumina 68-72%, Fire Crete Super Castable Refractory ( Type -70% Al Castable, Nature Of Bond –Castable Insulation ) , Refractory Supercastable Alumina 68-72%, Fire Crete Super Castable Refractory ( Type -70% Al Castable, Nature Of Bond –Castable Insulation ) ( Specification ( Al2o3:82.5-85.5%, Fe2o3:0.50-0.85, Max Service Temp:1700Oc, Max Grain Size:3Mm, Pre-8 Liquid For Ramming:9.7-10.7%, Dry Density:2.70-2.85G / Cc ( After Drying At 110Oc / 24Hrs ) , Ccs:260- 430Kg / Cm2 ( After Dryingat 110Oc / 24Hrs ) , Refractoriness, Orton / Oc Plc, % ( After Heating At 550Oc / 3Hrs: -0.3 To +0.3; After Heating At 815Oc / 3Hrs: -0.3 To +0.3 , Refractory Plastic Alumina 82.5-85.5, Plastic Refractory As Per Following Specification:Al2o3:82.5-85.5%, Fe2o3:0.50-0.85, Max Service Temp:1700 °C, Max Grain Size:3Mm, Pre-8 Liquid For Ramming:9.7-10.7%, Dry Density :2.70-2.85 G / Cc, ( After Drying At 110 °C / 24 Hrs ) , Ccs:260-430 Kg / Cm2 ( After Drying At 110 °C / 24 Hrs ) Refractoriness, Orton / °C Plc, % ( After Heating At 550 °C / 3Hrs: -0.3 To +0.3 ) After Heating At 815 °C / 3 Hrs: -0.3 To +0.3 ) After Heating At 1400Oc / 3Hrs: -1.60 To +1.70 ) , Refractory Supercastable Alumina 68-72%, Fire Crete Super Castable Refractory ( Type -70% Al Castable, Nature Of Bond –Castable Insulation ) , Fire Crete Refectory, Fire Crete Refectory -As Per Following Specification:Al2o3:68-72%, Cao:5.2-6%, Fe2o3:4.8-5.5%, Max Service Temp:1450 °C, Max Grain Size:5Mm, Water Required For Casting:10-11%, Dry Density:2.50-2.65 G / Cc, ( After Drying At 110 °C / 24 Hrs ) , Ccs:350-450 Kg / Cm2 ( After Drying At 110 °C / 24 Hrs ) Refractoriness, Orton / °C Plc, % ( After Heating At 1100 Deg C / 3Hrs:-0.30 To +0.30 ) After Heating At 1400 Deg C / 3 Hrs:-1.60 To +1.70 )

INR 1180 /-

INR 15000.0 /-

Refer document

Name of Work: Supply of Plastic Refractory and Super Castable Refractory

Sl. No.	Item Description
1	REFRACTORY SUPERCASTABLE ALUMINA 68-72%, Super Castable RefractoryAs per Following Specification:Al2O3:68-72%, CaO:5.2-6%, Fe2O3:4.8-5.5%, Max Service Temp:1450 °C, Max Grain Size:5mm, Water required for casting:10-11%, Dry Density:2.50-2.65 g/cc, (After drying at 110 °C/24 Hrs), CCS:350-450 Kg/Cm2( after drying at 110 °C/24 Hrs) Refractoriness, Orton/°C PLC, % (After Heating at 1100 deg C/3Hrs:-0.30 to +0.30) After heating at 1400 deg C/3 Hrs:-1.60 to +1.70)
2	REFRACTORY PLASTIC ALUMINA 82.5-85.5, Plastic refractory As per Following Specification:Al2O3:82.5-85.5%, Fe2O3:0.50-0.85, Max Service Temp:1700 °C, Max Grain Size:3mm, PRE-8 Liquid for ramming:9.7-10.7%, Dry Density :2.70-2.85 g/cc, (After drying at 110 °C/24 Hrs), CCS:260-430 Kg/Cm2( after drying at 110 °C/24 Hrs) Refractoriness, Orton/°C PLC, % (After Heating at 550°C/3Hrs:-0.3 to +0.3) After heating at 815 °C/3 Hrs: -0.3 to +0.3)
3	REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND #CASTABLE INSULATION)
4	REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND –CASTABLE INSULATION)
5	REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND –CASTABLE INSULATION) (Specification (Al2O3:82.5-85.5%,Fe2O3:0.50-0.85, Max Service Temp:1700oC, Max grain size:3mm, PRE-8 Liquid for ramming:9.7-10.7%, Dry density:2.70-2.85g/cc(After drying at 110oC/24Hrs), CCS:260- 430Kg/Cm2 (after dryingat 110oC/24Hrs),Refractoriness, Orton/oC PLC, %(After Heating at 550oC/3Hrs: -0.3 to +0.3; After Heating at 815oC/3Hrs: -0.3 to +0.3
6	REFRACTORY PLASTIC ALUMINA 82.5-85.5,PLASTIC REFRACTORY AS PER FOLLOWING SPECIFICATION:AL2O3:82.5-85.5%, FE2O3:0.50-0.85, MAX SERVICE TEMP:1700 °C, MAX GRAIN SIZE:3MM, PRE-8 LIQUID FOR RAMMING:9.7-10.7%, DRY DENSITY :2.70-2.85 G/CC, (AFTER DRYING AT 110 °C/24 HRS), CCS:260-430 KG/CM2( AFTER DRYING AT 110 °C/24 HRS) REFRACTORINESS, ORTON/°C PLC, % (AFTER HEATING AT 550 °C/3HRS: -0.3 TO +0.3) AFTER HEATING AT 815 °C/3 HRS: -0.3 TO +0.3)After Heating at 1400oC/3Hrs: -1.60 to +1.70)
7	REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND –CASTABLE INSULATION)
8	FIRE CRETE REFECTORY, FIRE CRETE REFECTORY -As per Following Specification:Al2O3:68-72%, CaO:5.2-6%, Fe2O3:4.8-5.5%, Max Service Temp:1450 °C, Max Grain Size:5mm, Water required for casting:10-11%, Dry Density:2.50-2.65 g/cc, (After drying at 110 °C/24 Hrs), CCS:350-450 Kg/Cm2( after drying at 110 °C/24 Hrs) Refractoriness, Orton/°C PLC, % (After Heating at 1100 deg C/3Hrs:-0.30 to +0.30) After heating at 1400 deg C/3 Hrs:-1.60 to +1.70)