Supply Of Tricast Wearcrete , Specification Service Temperature(Max.) 1650 Deg.C, Refractoriness 1785 Deg.C,Grain Size(Max) 6.0Mm, Mwthod Of Application -Ramming(Hand/Machine), Binder Requirement 10-11%, Al2o3 (Min) 80 (+/- 2)%, Fe2o3(Max) 0.3%, P2o5 (Max) 4%, , Bulk Density (Min) 2.7 Gm/Cc At 110Deg.C, Cold Crushing Strength(Min) 450 Ksc St 110 Deg.C/24 Hrs, 600 Ksc At 1000 Deg.C/5Hrs, 875 Ksc At 1300 Deg.C, Plc (Max) +/-(0.2) At 550 Deg.C/10Hrs, +/-(0.3) At 1000 Deg.C/5Hrs,+/-(0.6) At 1300 Deg.C/5Hrs, Mor(Min) 125Ksc Dried At 110Deg.C/24 Hrs, 200Ksc Fired At 1000Deg.C/5 Hrs,Abrasion Loss (Astm C704) 3.5Cc Fired At 850Deg.C/5Hrs, Mor Loss 20%( Astm C1171), Thermal Conductivity (Min) 2 Kcal/M/Hr/Deg.C At 1000 Deg.C, Special Grade Refractory Mortar Suitable For Fixing Bricks In Target Area With The Following Specification Service Temperature(Max.)1500 Deg.C, Raw Material Base Low Iron Fire Clay,Pce 31/ 1683 Ortan/Deg.C, Grain Size 0-0.5Mm, Al2o3 (Min) 52%, Sio2(Max.) 43%, Fe2o3(Max) 1%, Special Grade Refractory Mortar For Fixing Bricks In Non Target Area, Fgd Area As Per The Following Specification: Service Temperature(Max.)1250 Deg.C, Raw Material Base Fire Clay,Pce 20/1564 Ortan/Deg.C, Grain Size 0-0.5Mm, Al2o3 (Min) 40.5%, Sio2(Max.) 55%, Fe2o3(Max) 1.7%, Bulk Density (Min) 1.3 Gm/Cc, , Thermal Conductivity(Max) 1.2W/Mk At 300Deg.C, 1.3W/Mk At 700 Deg.C, 1.4W/Mk At 1100Deg.C, ,Refractory Castable Specification: Raw Material -Fire Clay, Al2o3 (Min.) 50%, Fe2o3 (Max.) 1%, Cao (Max.) 3%, Service Temperature 1550 Deg Centegrade, Grain Size 0-6Mm, Bulk Density 2.3Gm/Cc, Linear Change Of Length Irrerversible (Max.) At 1500 Deg Centegarde -0.9, Linear Change Of Length Reversible At 1000 Deg Centegrade 2.27, Thermal Condutivity (Max.) At 500Deg Centegrade 1.1 W/Mk, At 1000 Deg Centegrade 1.15 W/Mk, Cold Crushing Strength (Min.) At 110 Deg Centegarde 80N/Mm2, At 1200 Deg Centegrade 70N/Mm2, Packing -The Castables Have To Be Packed In 50 Kg Water Proof Bags