Supply Of Tricast Wearcrete , Specification Service Temperature(Max.) 1650 Deg.C, Refractoriness 1785 Deg.C,Grain Size(Max) 6.0Mm, Mwthod Of Application -Ramming(Hand/Machine), Binder Requirement 10-11%, Al2o3 (Min) 80 (+/- 2)%, Fe2o3(Max) 0.3%, P2o5 (Max) 4%, , Bulk Density (Min) 2.7 Gm/Cc At 110Deg.C, Cold Crushing Strength(Min) 450 Ksc St 110 Deg.C/24 Hrs, 600 Ksc At 1000 Deg.C/5Hrs, 875 Ksc At 1300 Deg.C, Plc (Max) +/-(0.2) At 550 Deg.C/10Hrs, +/-(0.3) At 1000 Deg.C/5Hrs,+/-(0.6) At 1300 Deg.C/5Hrs, Mor(Min) 125Ksc Dried At 110Deg.C/24 Hrs, 200Ksc Fired At 1000Deg.C/5 Hrs,Abrasion Loss (Astm C704) 3.5Cc Fired At 850Deg.C/5Hrs, Mor Loss 20%( Astm C1171), Thermal Conductivity (Min) 2 Kcal/M/Hr/Deg.C At 1000 Deg.C , Refractory Castable Specification: Raw Material -Bauxite, Al2o3 (Min.) 78%, Fe2o3 (Max.) 1.0%, Cao (Max.) 3.1%, Service Temperature 1600 Deg Centegrade, Grain Size 0-6Mm, Bulk Density 2.7Gm/Cc, Linear Change Of Length Irrevresible (Max.) At 1200 Deg Centegarde -/+0.4,At 1400 Deg Centegarde -/+0.1, Thermal Condutivity (Max.) At 500Deg Centegrade 2.15 W/Mk, At 1000 Deg Centegrade 1.95 W/Mk, Cold Crushing Strength (Min.) At 110 Deg Centegarde 80N/Mm2, At 1200 Deg Centegrade 110N/Mm2, Packing -The Castables Have To Be Packed In 50 Kg Water Proof Bags In Printed Particulars Of Suppliers/Manufacturers, Barnd Name And Name Of Material, Batch No. And Month, Year Of Manufacturer, Shelf Life And Weight Of Material. , Refractory Patch Up Material Specification: Raw Material -Calcined Clay/Calcined Bauxite, Al2o3 (Min.) 60%, Fe2o3 (Max.) 1.5%, Cao (Max) 2.5%,Service Temperature 1600 Deg Centegrade, Grain Size Maximum -5Mm, Bulk Density 2.5Gm/Cc, Plc At 1500 Deg Centegarde -/+1.0 (Max), Cold Crushing Strength (Min.) At 110 Deg Centegarde 50N/Mm2, At 1100 Deg Centegrade 60N/Mm2, Packing - The Tri Patch Material Have To Be Packed In 50/25 Kg Water Proof Bags In Printed Particulars Of Suppliers/Manufacturers, Brand Name And Name Of Material,