supply of wear resistant compound for various application in ash handling system and coal mill of 210 mw atps, mppgcl, chachai. , belzona 1812, ceramic carbide/loctite pac 7226 pneuwear compund/devcon wear guard high temp. or equivalent (two part ceramic bid filled epoxy compound for extensive abrasion mixing ratio - 4:1 working life - 20 minutes at 250 c self life - 05 yearsdry heat resistance - 200 degree certigrade compressive strength - 89 mpa post cure volume capacity - 484.5 cm3/kg mixed density -2.06g/cm3 flexural strength - 60 mpa, post cure , belzona 1111, super metalor equivalent (eposy composite reinforced with silicon steel alloy and fully machinable) mixing ratio - 3:1 working life - 15 minutes at 250 c self life - 05 yearsdry heat resistance - 2000c compressive strength - 66.3 mpa volume capacity - 398 cm3/kg mixed density -2.41-2.61 g/cm3 colour : light grey peak exotherm temperature: 950 c-1100c slump resistance : nil at 0.5 inch (1.27 cm) dielectric strength : 2.2 kv/mm, when tested to astm d149 at 1v& 2000 v/s dissipation factor : 0.09 meter, when tested & astm d 150 at 1 v & 10 khz , belzona 9111, cleaner/degreaser/loctite sf 7633/devcon surface cleaner or equivalent (cleaning the dust/impurities/pinats/blasting remainings etc at steel, copper, aluminium, pvc etc equipments) appearance : liquid colour : water white flash point : >630c cc vapour pressure : 0.03 kpa @ 200c relative density : 0.72-82@150c solubility : immiscible with water auto ignition temprature : >2000c , belzona 1311, ceramic r-metal or equivalent (eposy composite reinforced with silicon steel alloy and ceramic particles) mixing ratio - 3:1 (by volume) working life - 15 minutes at 250 self life - 05 yearsdry heat resistance - 2000c compressive strength - 56.8 mpa volume capacity - 415 cm3/kg mixed density -2.36-2.52 g/cm3 colour : light greypeak exotherm temperature: 990c-1100c slump resistance : nil at 0.5 inch (1.27 cm) , brushable ceramic/loctite pac 7333 nordbak or equivalent maximum temp. 1250 c working time 30 min. cure time 6 hrs.