tender for procurement of heat resistance paint tests at nabl accredited laboratory.; 1 list of tests 2 odor test - as per standerd astm d1296 3 volatile organic compounds voc content- as per standerd astm d2369- is 101 part 8-sec 2 4 pot life and viscosity of hrp mixture- as per standerd bs en iso 2431 or astm d 1200 or is101 part 1 sec 5 5 drying time- as per standerd astm d1640 or is 101 part 3, sec 1 6 density- as per standerd astmd1475 oris 101 part 1, sec 7 7 specular gloss- as per standerd bs 2782-5 520a or is- 101-part-4-sec-4 8 dry film thickness- as per standerd astm e376or astm b499 9 bend- flexibility test room temperature - as per standerd astm b571 or is 101 part 5 sec 2 10 bend- flexibility test low temperature- as per standerd is 101 part 5 sec 2 for reference 11 adhesion cross hatch- as per standerd astm d 3359 test method a-b or bs3900-part e6, 1 mm spacing 12 adhesion dolly test- as per standerd astm d4541 13 hardness scratch test- as per standerd astm d3363 - is 101 part 5 sec 1 14 water resistance- as per standerd astm d870 for 168 hrs 15 fuel resistance (atf k-50) - as per standerd astm d 6943 16 gearbox oil resistance (oep-70)- as per standerd astm d 6943 17 hydraulic oil (h-515)- as per standerd astm d 6943 for 168 h at 40 c 18 grease resistance (g382, g366, g355) - as per standerd astm d 6943 for 168 h at 40 c 19 weather resistance- as per standerd astm g155duration 500 h chamber condition: temp: 42 ±3 °c 20 high temperature test- as per standerd mil-std-810g method 501-5 for 24 hour temperature up to 200 °c 21 low temperature - as per standerd test mil-std-810g method 502-5 procedure-ii 4 h 22 salt spray- as per standerd mil-std-810 g method 509-5for 96 h 23 combined altitude temperature and humidity test cath- as per standerd mil-std-810g (cycles: 10 cycles) (1 cycle=16 h) 24 resistance to dust- as per standerd mil-std-810g method 510-5 jss 55555 test no 14 25 resistance to rain driving rain- as per standerd mil- std-810g method 506-5- jss 55555 26 vibration test- as per standerd mil-std-810g method 514-6(main rotor frequency: 5.88hzf=5.88hz, a 1=0.144g f1 =17.65hz, a2=1.765g) 27 thermal shock- as per standerd mil-std-810g method 503-5 procedure i-b 28 humidity resistance- as per standerd mil-std-810g, method 507-5 29 icing-freezing rain- as per standerd mil-std-810g method 521-3- jss 55555