supply of cut gasket , cut gasket , size: 1x150#; i . d: 25mm; o . d: 60mm; thickness: 3mm; moc : 100% ptfe , bi-axially expanded , without fillers < ( >&< ) > pigments . - service : all concentrations of sulpuric < ( >&< ) > nitric acid . -temperature : suitable to working at 250 deg . celcius min . - pressure range: vacuum upto 2900 psi ( 200 bar ) or higher - density : 0 . 8 to 0 . 9 g/cm3 - compressibility ( as per astm f36 ) : 35% to 60% - recovery ( as per astm f36 ) : 12% to 14% - make: gore / ukl / teadit / kwo / equi . - self certified test reports for compressibility < ( >&< ) > recovery to be furnished along with supply of material . , cut gasket , size: 1-1/2x150#; i . d: 40mm; o . d: 80mm; thickness: 3mm . ; moc : 100% ptfe , bi-axially expanded , without fillers < ( >&< ) > pigments . - service : all concentrations of sulpuric < ( >&< ) > nitric acid . - temperature : suitable to working at 250 deg . celcius min . - pressure range: vacuum upto 2900 psi ( 200 bar ) or higher - density : 0 . 8 to 0 . 9 g/cm3 - compressibility ( as per astm f36 ) : 35% to 60% - recovery ( as per astm f36 ) : 12% to 14% - make: gore / ukl / teadit / kwo / equi . - self certified test reports for compressibility < ( >&< ) > recovery to be furnished along with supply of material . , cut gasket , size: 4x150#; i . d: 100 mm; o . d: 160 mm; thickness: 3mm . ; moc : 100% ptfe , bi-axially expanded , without fillers < ( >&< ) > pigments . - service : all concentrations of sulpuric < ( >&< ) > nitric acid . - temperature : suitable to working at 250 deg . celcius min . - pressure range: vacuum upto 2900 psi ( 200 bar ) or higher - density : 0 . 8 to 0 . 9 g/cm3 - compressibility ( as per astm f36 ) : 35% to 60% - recovery ( as per astm f36 ) : 12% to 14% - make: gore / ukl / teadit / kwo / equi . - self certified test reports for compressibility < ( >&< ) > recovery to be furnished along with supply of material . , ready cut gasket 1 ) flange size: 6x150# 2 ) gasket size: 168 mm ( id ) x 222 mm ( od ) . 3 ) thickness: 3mm . 4 ) material: 100% ptfe , bi-axially expanded , without fillers < ( >&< ) > pigments . 5 ) service: all concentrations of sulpuric < ( >&< ) > nitric acid . 6 ) service temperature : suitable to working at 250 deg . celcius min . 7 ) service pressure range: vacuum upto 2900 psi ( 200 bar ) or higher 8 ) density : 0 . 8 to 0 . 9 g/cm3 9 ) compressibility ( as per astm f36 ) : 35% to 60% 10 ) recovery ( as per astm f36 ) : 12% to 14% 11 ) make: gore / ukl / teadit / kwo / equi . note : 1 ) vendor to furnish self certified test reports for compressibility < ( >&< ) > recovery along with the supply of material . , cut gasket , size: 8x150#; i . d: 205mm; o . d: 238mm; thickness: 3mm; moc : 100% ptfe , bi-axially expanded , without fillers < ( >&< ) > pigments . - service : all concentrations of sulpuric < ( >&< ) > nitric acid . - temperature : suitable to working at 250 deg . celcius min . - pressure range: vacuum upto 2900 psi ( 200 bar ) or higher - density : 0 . 8 to 0 . 9 g/cm3 - compressibility ( as per astm f36 ) : 35% to 60% - recovery ( as per astm f36 ) : 12% to 14% - make: gore / ukl / teadit / kwo only . , cut gasket , size: 2x150#; i . d: 50mm; o . d: 100mm; thickness: 3mm . ; moc : 100% ptfe , bi-axially expanded , without fillers < ( >&< ) > pigments . - service : all concentrations of sulpuric < ( >&< ) > nitric acid . - temperature : suitable to working at 250 deg . celcius min . - pressure range: vacuum upto 2900 psi ( 200 bar ) or higher - density : 0 . 8 to 0 . 9 g/cm3 - compressibility ( as per astm f36 ) : 35% to 60% - recovery ( as per astm f36 ) : 12% to 14% - make: gore / ukl / teadit / kwo / equi . - self certified test reports for compressibility < ( >&< ) > recovery to be furnished along with supply of material . , cut gasket , size: 3x150#; i . d: 75mm; o . d: 127mm; thickness: 3mm ; moc : 100% ptfe , bi-axially expanded , without fillers < ( >&< ) > pigments . - service : all concentrations of sulpuric < ( >&< ) > nitric acid . - temperature : suitable to working at 250 deg . celcius min . - pressure range: vacuum upto 2900 psi ( 200 bar ) or higher - density : 0 . 8 to 0 . 9 g/cm3 - compressibility ( as per astm f36 ) : 35% to 60% - recovery ( as per astm f36 ) : 12% to 14% - make: gore / ukl / teadit / kwo / equi . - self certified test reports for compressibility < ( >&< ) > recovery to be furnished along with supply of material .