Bids Are invited for Ms Plate Thick - 12Mm , Pm Plate Sail Hard 16 Mm 16X2500x12000 - Sailhard Pm Plate Of 16Mm(Thickness) X 2500 Mm (Width) X 12000Mm(Length) Size Untrmd. Composition- Carbon 0.23 Percent(Max), Manganese 1.6 Percent(Max), Phosphorus 0.05 Percent(Max), Sulphur 0.05 Percent(Max), Silicon 0.50Percent (Max), Aluminium 0.1 Percent(Max), Chromium 0.65 Percent(Max), Nb+V+Ti 0.15 Percent(Max), Hardness 200 Bhn(Min) , Mill Plate Sail Hard 20Mmx2500x12500 - Sailhard Pm Plates Of 20Mm(Thickness) X 2500Mm(Width) X 12500Mm(Length) Size Untrimd. Composition- Carbon 0.23 Percent(Max), Manganese 1.6 Percent(Max), Phosphorus 0.05 Percent(Max), Sulphur 0.05 Percent(Max), Silicon 0.50 Percent (Max), Aluminium 0.1 Percent(Max), Chromium 0.65 Percent(Max), Nb+V+Ti 0.15 Percent(Max), Hardness 200 Bhn(Min). , Mill Plate Sailhard 12 Mm X2500x12500 - Sailhard Pm Plate Of 12Mm(Thickness)X2500mm(Width)X 12500Mm(Length) Size Untrmd. Composition- Carbon 0.23 Percent(Max), Manganese 1.6 Percent(Max), Phosphorus 0.05 Percent(Max), Sulphur 0.05 Percent(Max), Silicon 0.50 Percent(Max), Aluminium 0.1 Percent(Max), Chromium 0.65 Percent(Max), Nb+V+Ti 0.15 Percent(Max), Hardness 200 Bhn(Min). , C.S Plate Of Size 5Mm - Dimension- 5Mmx1250mmx2500mm, Composition- Carbon 0.25-0.29 Percent, Iron 98 Percent, Manganese 0.80-1.20 Percent, Silicon 0.15-0.40 Percent, Phosphorus Less Than Or Equal To 0.05 Percent, Copper 0.20 Percent, Tensile Strength 274-450 Mpa, Hardness 119-162 Bhn, Confirming To Astm A36 Standards. , Carbon Steel Plate 25 Mm - Composition- Carbon 0.05-0.25 Percent, Manganese 1.03 Percent, Silicon 0.05 Percent, Phosphorus 0.04 Percent, Copper 0.2 Percent, Tensile Strength 275-450 Mpa, Hardness 120 Bhn, Confirming To Astm A36 Standards. , Carbon Steel Plate 10 Mm - Composition- Carbon 0.05-0.25 Percent, Manganese 1.03 Percent, Silicon 0.05 Percent, Phosphorus 0.04 Percent, Copper 0.2 Percent, Tensile Strength 275-450 Mpa, Hardness 120 Bhn, Confirming To Astm A36 Standards. Tot