Bids Are Invited For Non Ferrous Welding Consumables - Er 4043 - 1.2 Mm Er 4043 - 1.6 Mm Er 4043 - 2.4 Mm Er 5356 - 1.2 Mm Er 5356 - 1.6 Mm Er 5356 - 2.4 Mm Er 5183 - 1.2 Mm Er 5183 - 1.6 Mm Er 5183 - 2.4 Mm Er 5556 - 1.2 Mm Er 5556 - 1.6 Mm Er

Sharing tender

Bids Are Invited For Non Ferrous Welding Consumables - ER 4043 - 1.2 mm ER 4043 - 1.6 mm ER 4043 - 2.4 mm ER 5356 - 1.2 mm ER 5356 - 1.6 mm ER 5356 - 2.4 mm ER 5183 - 1.2 mm ER 5183 - 1.6 mm ER 5183 - 2.4 mm ER 5556 - 1.2 mm ER 5556 - 1.6 mm ER 5556 - 2.4 mm ERTi-5 - 1.2 mm ERTi-5 - 1.6 mm ERTi-5 - 2.4 mm ERTi-23 - 1.2 mm ERTi-23 - 1.6 mm ERTi-23 - 2.4 mm 1 ER 4043 - 1.2 mm Size 1.2 mm diameter layer wound Spools on S300 spool with 7Kg weight. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, cast and helix, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA 5.10M. Precision layer and level winding are essential. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 35.00 KG 28 DAYS 2 ER 4043- 1.6 mm Size 1.6 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 3 ER 4043 - 2.4 mm Size 2.4 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 4 ER 5356 -1.2 mm Size 1.2 mm diameter layer wound Spools on S300 spool with 7Kg weight. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, cast and helix, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA 5.10M. Precision layer and level winding are essential. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 35.00 KG 28 DAYS 5 ER 5356- 1.6 mm Size 1.6 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 6 ER 5356 - 2.4 mm Size 2.4 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 7 ER 5183 -1.2 mm Size 1.2 mm diameter layer wound Spools on S300 spool with 7Kg weight. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, cast and helix, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA 5.10M. Precision layer and level winding are essential. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 35.00 KG 28 DAYS 8 ER 5183- 1.6 mm Size 1.6 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 9 ER 5183 - 2.4 mm Size 2.4 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 10 ER 5556 -1.2 mm Size 1.2 mm diameter layer wound Spools on S300 spool with 7Kg weight. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, cast and helix, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA 5.10M. Precision layer and level winding are essential. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 35.00 KG 28 DAYS 11 ER 5556 - 1.6 mm Size 1.6 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 12 ER 5556 - 2.4 mm Size 2.4 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.10/SFA-5.10M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 30.00 KG 28 DAYS 13 ER Ti-5 -1.2 mm Size 1.2 mm diameter layer wound Spools on S300 spool. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, cast and helix, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.16/SFA 5.16M. Precision layer and level winding are essential. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 80.00 KG 28 DAYS 14 ER Ti-5 - 1.6 mm Size 1.6 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.16/SFA-5.16M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 50.00 KG 28 DAYS 15 ER Ti-5 - 2.4 mm Size 2.4 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.16/SFA-5.16M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 50.00 KG 28 DAYS 16 ER Ti-23 -1.2 mm Size 1.2 mm diameter layer wound Spools on S300 spool. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, cast and helix, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.16/SFA 5.16M. Precision layer and level winding are essential. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 80.00 KG 28 DAYS 17 ER Ti-23- 1.6 mm Size 1.6 mm diameter X 900 to 1000 mm length Cut to length should be with embossing/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.16/SFA-5.16M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. 50.00 KG 28 DAYS 18 ER Ti-23 - 2.4 mm Size 2.4 mm diameter X 900 to 1000 mm length Cut to length should be with embossingP/imprinting on at least one end for positive identification. Chemical composition, Mechanical properties, finish and uniformity, method of manufacture, tolerance, identification, packaging, marking of packages, all tests and acceptance criteria shall be as per ASME Section II Part C SFA-5.16/SFA-5.16M. Lot classification: S1, Schedule of testing: 5 or J. The weld using this consumable shall exhibit radiographic soundness with 100% Argon shielding and shall flow freely uniformly without any defects. Total Quantity : 740