Tender For 40002263 - Refractory Castable

Sharing tender

Tender For 40002263 - Refractory Castable 40002263 0001 0001 201100332 GUNNING MASS,MONOLITHIC,Al2O3:67% Technical Details Name : Vijay Kumar Kunche Contact : Email : [email protected] 70 TO GUNNING MASS TYPE : MONOLITHIC REFRACTORY , MgO : 0.5 PERCENTAGE CaO : 2.5 PERCENTAGE , SiO2 : 28 PERCENTAGE Fe2O3 : 0.8 PERCENTAGE , Al2O3 : 67 PERCENTAGE SERVICE TEMPERATURE : 1750 DEG.C , FORM : POWDER GRAIN SIZE : 4 MESH ADDITIONAL INFORMATION : HIGH STRENGTH ABRASION RESISTANT SPECIAL GUN MIX. Item Details : PCPF Surgun R70A by M/s Vesuvius design Item Note : 2 40002263 0002 0002 201108570 REFRACTORY,CASTABLE,GUNNING,Al2O3-40% Technical Details Name : Vijay Kumar Kunche Contact : Email : [email protected] 15 TO REFRACTORY,CASTABLE TYPE : GUNNING MASS , INSTALLED YIELD : 90 PERCENT Al2O3 CONTENT : 40 PERCENT , SiO2 CONTENT : 48 PERCENT Fe2O3 CONTENT : 3.5 PERCENT , CaO CONTENT : 5 PERCENT SERVICE TEMPERATURE : 1370 DEG.C , BULK DENSITY : 2.1 GM/CM3 COLD CRUSHING STRENGTH MIN : 100 KG/CM2 , MAX GRAIN SIZE : 5 MM Item Details : PCPF Litewate 6009 LiHT by M/s Vesuvius Item Note : 3 40002263 0003 0003 201109525 CASTABLE,RFCTY,INSULATING,AL2O347%,1300 Technical Details Name : Vijay Kumar Kunche Contact : Email : [email protected] 3 TO CASTABLE,REFRACTORY TYPE:INSULATING , MAJOR CHEMICAL COMPOSITION:AL2O3 47 % SERVICE TEMPERATURE:1300 °C CHEMICAL COMPOSITION OF REMAINING:FE2O3 1.5, CAO 10, SIO2 41.5 %(M) GRAIN SIZE:5 MM , COLD CRUSHING STRENGTH (CCS):12 MPA BULK DENSITY:1.6 G/CM3 , TYPE OF BOND:HYDRAULIC PERMANENT LINEAR CHANGE (PLC):-0.3 % , THERMAL CONDUCTIVITY:0.5 SHELF LIFE:6 MONTHS , ADDITIONAL INFORMATION:LITEWATE 6016 Item Details : Litewate 6016 for inspection doors by M/s Vesuvius Item Note : 4 40002263 0004 0004 201109414 BLOK,RFCTY,DRG:AR05257,PRECST,770MM,AL2 Technical Details Name : Vijay Kumar Kunche Contact : Email : [email protected] 4 NO BLOCK,REFRACTORY TYPE:PRE CAST , SIZE:770 MM MAJOR CHEMICAL COMPOSITION:AL2O3- 73 % , SHAPE:RECTANGLE CHEMCIAL COMPOSITION OF REMAINING:SIO2- 21, FE2O3- 0.8, CAO-2 % SERVICE TEMPERATURE:1700 °C COLD CRUSHING STRENGTH (CCS):100 (@110 DEG.C) MPA BULK DENSITY:2.8 G/CM3 , ADDITIONAL INFORMATION:BURNER BLOCK ASSEMBLY DRAWING DRG NO:AR05257 , DRAWING REV NO:0 Item Details : PCPF Burner Blocks including metallic part by M/s Vesuvius Item Note : 5 40002263 0005 0005 201109142 BLOK,RFCTY,PRECST,3000MM,AL2O383% Technical Details Name : Vijay Kumar Kunche Contact : Email : [email protected] 40 NO BLOCK,REFRACTORY TYPE:PRE CAST , SIZE:3000 MM MAJOR CHEMICAL COMPOSITION:AL2O3 83 % , SHAPE:RECTANGLE CHEMCIAL COMPOSITION OF REMAINING:SIO2-10, FE2O3-1, CAO-2.6 % SERVICE TEMPERATURE:1550 °C , COLD CRUSHING STRENGTH (CCS):1100 MPA BULK DENSITY:2.95 G/CM3 , DRAWING DRG NO:AR04626 DRAWING REV NO:1 Item Details : Dry Seal Box by M/s Vesuvius Item Note : 6 40002263 0006 0006 201109140 BLOK,RFCTY,PRECST,371MM,AL2O395% Technical Details Name : Vijay Kumar Kunche Contact : Email : [email protected] 160 NO BLOCK,REFRACTORY TYPE:PRE CAST , SIZE:371 MM MAJOR CHEMICAL COMPOSITION:AL2O3 95 % , SHAPE:SPECIAL CHEMCIAL COMPOSITION OF REMAINING:SIO2-1, FE2O3-0.05 % SERVICE TEMPERATURE:1800 °C , COLD CRUSHING STRENGTH (CCS):700 MPA BULK DENSITY:2.85 G/CM3 , PERMANENT LINEAR CHANGE (PLC):0.2 % DRAWING DRG NO:AR04632 , DRAWING REV NO:2 Item Details : Dry lintel blocks - FZDL1 160 nos. by M/s Vesuvius Item Note : 7 40002263 0007 0007 201109140 BLOK,RFCTY,PRECST,371MM,AL2O395% Technical Details Name : Vijay Kumar Kunche Contact : Email : [email protected] 25 NO BLOCK,REFRACTORY TYPE:PRE CAST , SIZE:371 MM MAJOR CHEMICAL COMPOSITION:AL2O3 95 % , SHAPE:SPECIAL CHEMCIAL COMPOSITION OF REMAINING:SIO2-1, FE2O3-0.05 % SERVICE TEMPERATURE:1800 °C , COLD CRUSHING STRENGTH (CCS):700 MPA BULK DENSITY:2.85 G/CM3 , PERMANENT LINEAR CHA