Haryana Power Generation Corporation Limited-HPGCL has published Tender For Supply Of Boiler Refractory. Submission Date for this Tender is 16-05-2024. Boiler Supply Tenders in Yamunanagar Haryana. Bidders can get complete Tender details and download the document.
Sr No | CorrigendumDate | Corrignedum | CorrigendumType | NewSubmissionDate |
1 | 22-Dec-2023 | corrigendum | Date | 11-01-2024 |
2 | 12-Jan-2024 | Extension | Date | 01-02-2024 |
3 | 05-Feb-2024 | corrigendum1 | Date | 22-02-2024 |
4 | 23-Feb-2024 | corrigendum3 | Date | 14-03-2024 |
5 | 18-Mar-2024 | Corrigendum | Date | 04-04-2024 |
6 | 08-Apr-2024 | DATE | Date | 25-04-2024 |
7 | 29-Apr-2024 | Corrigendum1 | Date | 16-05-2024 |
FileName | File Description | File Size |
0dbdfe48-a696-452c-844d-30fb02b3aedb.html | Tender Notice | 0 KB |
BOQ_407470.xls | Tender Document | 0 KB |
Tendernotice_1.pdf | Tender Document | 0 KB |
Sl. No. | Item Description |
1 | Castable refractory, equivalent to fire Crete special, service temp 1350 Deg. C PCE-1580 Deg. C Dry density Min-2100jg.Cynm Linear Change % Max. ± 1.54 at 1400 Deg C per 2 Hrs. CCS Min-250kg/Sq, Cm at 110 Deg. C, 225 Kg/Sq Cm at 1300 Deg C, A12O3 (Min)-45%, Fe2O3 (Max.)-4% Max grain size -5mm Testing Standard for Chemical analysis-IS:12107 for Physical properties-IS:10570 Making following details are to be legibly written on the bags Suppliers Name: Customer Name/Project. Purchase order No/Date Batch no. material name, Net weight in kgs shelf life in months. Packing the material shall be packed and sealed in polythene bags and the thickness of polythene bags shall be atleast 0.5mm. Then the sealed bags shall be put inside the polythene lined HOPE or HDPP woven netting base sad sealed by machine stiching. |
2 | High Alumina Binder for castable refractory Chemical composition LOI-0-50%, SIO2-5.60%, Fe2O3-4.20%, TiO2-6.60%, CaO-32.80%, AI2O3-49.00%, MgO-1.00%, Note-ACC or equivalent make. |
3 | Plastic Refractory with Liquid Binder with following specifications: 1. Chemically bonded plastic refractory (Two component system Powder & liquid to be supplied separately) 2. Chemical composition: AL2O3-87% (min) SIO2-6.5% Fe2O3-0.5%. (Max). 3. Physical properties: Dry density gm/cc, after drying at 2600C for 3 hrs -2.7 9min) Cold crushing strength kg/cm2. After drying at 2600C 3 hrs-150 (min) After heating at 15500C for 3 hrs-300 (min). |