| 1 | Painting in SEZ Area |
| 2 | HAND TOOL/MANUAL CLEANING TO SSPCSP-2 |
| 3 | SAND BLASTING TO SSPC SP6(With Compressor & Diesel IN CONTRACTOR SCOPE) |
| 4 | GRIT/COPPER SLAG BLASTING TO SSPC SP6 (WITH COMPRESSOR AND DIESEL IN CONTRACTOR SCOPE) |
| 5 | PRIMER COAT,ONECOAT OF EPOXY MASTIC,100 MICRON DFT(SELF PRIMING TYPESURFACE TOLERANT HIGH BUILD EPOXY COATING), P-2 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 6 | INTERMEDIATE COAT, ONE COAT OF EPOXY HIGH BUILD FINISH PAINT 100 MICRONS DFT, P-3 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 7 | FINISH COAT OF ONE COAT OF ACYRYLIC POLYURETHANE FINISH PAINT, 40 MICRONS DFT(WHITE/GREY), P-5 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 8 | FINISH COAT OF ONE COAT OF ACYRYLIC POLYURETHANE FINISH PAINT, 40 MICRONS DFT(RED), P-5 OF OMPL PAINT SPECOMPL/INSP/PAINT/SPEC - REV0 |
| 9 | THREE COATS OF HEAT RESISTANT ALUMINIUM PAINT SUITABLE FOR 250 DEG C,20 MICRONS DFT PER COAT,P-7 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 10 | THREE COATS OF HEAT RESISTANT SILICONE ALUMINIUM PAINT SUITABLE UPTO 500 DEG C ,20 MICRONS DFT PER COAT,P-8 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 11 | ONE COAT OF GLASS FLAKEEPOXY, 500 MICRON DFT,P-9 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 12 | TWO COATS OF EPOXY ZINC PHOSPHATE PRIMER,35 MICRONS DFT PER COAT,P-1 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 13 | FINISH COAT ,TWO COATS OF HIGHBUILD,EPOXY PHENOLIC AMINE BASED,100 MICRONS DFT PER COAT, P-10 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 14 | INTERMEDIATE COAT ,ONE COAT OF HIGHBUILD,EPOXY PHENOLIC AMINE BASED,100 MICRONS DFT PER COAT, P-10 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 15 | FINISH COAT ,TWO COATS OF HIGH BUILT COAL TAR EPOXY COATING,100 MICRONS DFT PER COAT, P-4 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 16 | FINISH COAT,THREE COATS OF HIGH BUILD COAL TAR EPOXY ,100 MICRONS DFT PER COAT,P-4 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 17 | COLOUR CODING MARK ON PROCESS LINES,OVER CLADDING /ON THE SURFACE WITHOUT ANY PAINTS/SS LINES-ONE COAT OF ACRYLIC POLYURETHANE/ENAMEL 40 MICRONS DFT.EACH COLOUR CODING MARK CONSISTING OF PRIMARY IDENTIFICATION COLOR BAND AND II & III BANDS SUPERIMPOSED ON THE PRIMARY BAND PAINTED CIRCUMFERENTIALLY AROUND THE LINE AS PER OMPL COLOR CODING STANDARD OMPL/INSP/COLCODE/SPEC -REV0 |
| 18 | TWO COATS OF POLYAMINE CURED EPOXY (SPECIALLY FORMULATED POLYAMINE CURED COAL TAR EPOXY SUITABLE FOR APPLICATION UNDER INSULATION),125 MICRONS DFT PER COAT,P-11 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 19 | THREE COATS OF EPOXY PHENOLIC COATING(TWO PACK AMBIENT TEMPERATURE CURING EPOXY PHENOLIC COATING) 85 MICRONS DFT PER COAT,P-12 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 20 | ONE COAT OF AMBIENT TEMPERATURE CURING POLYSILOXANE/INORGANIC COPOLYMER BASED ALUMINIUM COATING ,75 MICRONS DFT,P-13 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 21 | SCAFOLD FOR PAINTING WITH CONTR MATLS ERECTION OF SCAFFOLDING(WHEREVER REQUIRED DUE TO LACK OF ACCESS/SAFETY REQUIREMENT) WITH HIS OWN SCAFFOLDING MATERIAL, DISMANTLING OF SCAFFOLDING AFTER THE COMPLETION OF THE PAINTING JOBS INCLUSIVE OF TRANSPORTATION OF SCAFFOLDING MATERIAL TO THE JOB LOCATION.SCAFFOLDING AS PERSPECIFICATION/IS STD 3696(PART I) |
| 22 | Painting in Non SEZ Area |
| 23 | HAND TOOL/MANUAL CLEANING TO SSPCSP-2 |
| 24 | PRIMER COAT,ONECOAT OF EPOXY MASTIC,100 MICRON DFT(SELF PRIMING TYPESURFACE TOLERANT HIGH BUILD EPOXY COATING), P-2 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 25 | INTERMEDIATE COAT, ONE COAT OF EPOXY HIGH BUILD FINISH PAINT 100 MICRONS DFT, P-3 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 26 | FINISH COAT OF ONE COAT OF ACYRYLIC POLYURETHANE FINISH PAINT, 40 MICRONS DFT(WHITE/GREY), P-5 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 27 | ONE COAT OF GLASS FLAKEEPOXY, 500 MICRON DFT,P-9 OF OMPL PAINT SPEC OMPL/INSP/PAINT/SPEC - REV0 |
| 28 | SCAFOLD FOR PAINTING WITH CONTR MATLS ERECTION OF SCAFFOLDING(WHEREVER REQUIRED DUE TO LACK OF ACCESS/SAFETY REQUIREMENT & WITH PRIOR APPROVAL OF EIC) WITH HIS OWN SCAFFOLDING MATERIAL, DISMANTLING OF SCAFFOLDING AFTER THE COMPLETION OF THE PAINTING JOBS INCLUSIVE OF TRANSPORTATION OF SCAFFOLDING MATERIAL TO THE JOB LOCATION.SCAFFOLDING AS PER SPECIFICATION/IS STD 3696(PART I) |