Tenders Are Invited For Supply Of Welding Wires Of Various Types And Sizes Test Parameters: * Protective Medium - N/A; * Ampere / Polarity - 255 Medium / Dcen; * Volts - 20; * Wfs In/Min (M/Min) - 110 (2.8); * Eso In(Mm) - 1 (25); * Preheat F(C) - 300(149); * Interpass F(C) - 300(149); * Travel Speed Inch/Min (Cm/Min) - 6.2 (15.7); - Mechanical Properties - Tensile: * Protective Medium - N/A; * Test Conditions - Age 48 Hours 220F; * Ult. Tensile Strength Psi (Mpa) - 84,000 (580); * Yield Strength Psi (Mpa) - 71,000 (492); * Extension: % 2 - 26; - Mechanical Properties - Effect: * Protective Medium - N/A; * Test Conditions - As Welded; * Temp. F (C) - - 40(-40); * Individuals Ft.Lb.(J) - 124,114.99 (168,155,134); * Avg. Ft.Lb.(J) - 112 (152); * Type - Charpy-V-Notch. Chemical Composition: C - 0.04; Mn - 1.21; P - 0.007; S - 0.003; Si - 0.06; Cu - 0.03; Cr - 0.15; V - < .01; Ni - 0.82; Mo - < .01; Buy - 0.88 Aws A5.29 Asme Sfa5.29 Kg 2000 2 Welding Wire D=1.2Mm Ok Tubrod 15.17 Type Or Analog, Semi-Automatic For The Welding Machine * Welding Current - Dc+; * Diffuse Hydrogen - < 5 Ml/100G (M21 Gas) < 4 Ml/100G (C1 Gas); * * Alloy Type Low-Alloy Steel (1% Ni); - Typical Tensile Properties: * Yield Strength - 544 Mpa (79 Ksi); * Hardness Limit - 613 Mpa (89 Ksi); * Relative Elongation 26%; - Typical Weld Metal Analysis, %: * C-0.05, Mn-1.15, Si-0.34, Ni-0.96 - Information On It: * Diameter - 1.2 Mm, Current - 110- 300A, Voltage 21-32V, Wire Transmission Speed - 3.2-14.5 M/Min, Sedimentation Rate - 1.3-5.8 Kg/H Sfa/Aws A5.29 : E81t1-Ni1mj Sfa/Aws A5.29 : E81t1-Ni1cj H4 En Iso 17632-A : T 46 3 1Ni P C1 2 H5 En Iso 17632-A : T 46 4 1Ni P M21 2 H5 Kg 13500 3 Welding Wire D=1.2Mm Ok Tubrod 15.15 Type Or Analog, Semi-Automatic For The Welding Machine * Welding Current - Dc+; * Diffuse Hydrogen - < 5 Ml/100G; * Alloy Type C Mn; - Typical Tensile Properties: Aws In C1 Shielding Gas: Condition Pwht H 620 °C (1148 °F) * Yield Strength - 526 Mpa (76 Ksi); * Hardness Limit - 601 Mpa (87 Ksi); * Relative Elongation 25.4%; En In C1 Shielding Gas: As Welding * Yield Strength - 528 Mpa (77 Ksi); * Hardness Limit - 560 Mpa (81 Ksi); * Relative Elongation 27%; Sfa/Aws A5.20 : E71t-1C Sfa/Aws A5.20 : E71t-1M En Iso 17632-A : T 46 2 P C1 1 H5 En Iso 17632-A : T 46 2 P M21 2 H5 Kg 2500 6 - Typical Weld Metal Analysis, %: In M21 Shielding Gas: * C-0.06, Mn-1.40, Si-0.40 In C1 Shielding Gas: * C-0.05, Mn-1.31, Si-0.31 - Information On It: * Diameter - 1.2 Mm, Current - 110- 300A, Voltage 20-30V, Wire Transmission Speed - 3.2-14.5 M/Min, Sedimentation Rate - 1.3-5.8 Kg/H 4 Argon Welding Wire D=2.4 X 1000 Mm Tigrod 12.64 Type Or Analog * Alloy Type Carbon-Manganese Steel; - Typical Tensile Properties: Ar (I1) Aws: As Welding * Yield Strength - 510 Mpa (74 Ksi); * Hardness Limit - 610 Mpa (88 Ksi); * Relative Elongation 30%; Stress Relief: 2 Hours At 620 °C (1148 °F) * Yield Strength - 400 Mpa (58 Ksi); * Hardness Limit - 525 Mpa (76 Ksi); * Relative Elongation 32%; Ar (I1) En: As Welding * Yield Strength - 525 Mpa (76 Ksi); * Hardness Limit - 595 Mpa (86 Ksi); * Relative Elongation 26%; - Typical Weld Metal Analysis, %: According To Argon: * C-0.08, Mn-1.28, Si-0.80, S-0.013, P0.015 According To Carbon: * C-0.074, Mn-1.68, Si-0.95 - Information On It: * Diameter - 2.4 Mm, Current - 110- 300A, Voltage 20-30V, Wire Transmission Speed - 3.2-14.5 M/Min, Sedimentation Rate - 1.3-5.8 Kg/H Sfa/Aws A5.18: Er70s-6 En Iso 636-A : W 46 5 4Si1 En Iso 636-A : W 4Si1 100 Kg 5 Automatic Welding Wire D=3.2Mm Autrode 12.24 Type Or Similar For Manual Arc Welding Under Flux Molybdenum Alloyed Copper Clad Wire. High Temperature Resistant Steels (0.5% Mo), Structures Steels For Shipbuilding Steels, High Pressure Vessels And Pipe For Steels Up To X70 And For Belt Etc. - Typical Weld Metal Analysis, %: * C-0.009, Mn-1.08, Si-0.14, Mo-0.48 Sfa/Aws A5.23 : Ea2 En Iso 14171-A : S2mo En Iso 24598-A : S S Mo Kg 3500 6 Automatic Welding Flux Asfx-B110, Ok 10.71 Type Or Analog Welding Current - 900 A (60 X 0.5 Mm On The Line), Slag Type - Aluminate-Fluoride Base, Al2o3-Caf2, Alloy Permeability - Quiet Alloying With Silicon, Density - Nom: 1.1 Kg/Dm³, Basic Index - Nom: 2.5, - Typical Mechanical Properties: For Nicrmo-3 Wire: * Welding Condition - Hi ~1.0-1.6 Kj/Mm Dc+ * Yield Strength - 460 Mpa (67 Ksi); * Hardness Limit - 710 Mpa (103 Ksi); * Relative Elongation 44%; For Nicrmo-3 Saw Wire: Aws A5.17: Em12k Aws A5.17 : F7a4 - Em12k En 756 : S2si Kg 2500 7 * Welding Condition - Hi ~1.0-1.6 Kj/Mm Dc+ * Yield Strength - 460 Mpa; * Hardness Limit - 710 Mpa; * Relative Elongation 44%; - Typical Weld Metal Analysis, %: Nicrmo3 Dc+, 300A, 29V, Dia 2.4 Mm * C-0.01, Mn-0.1, Si-0.5, S-0.1, P-0.01, Ni-Bal., Cr-21.5, Mo-8.5, Cu-0.08, Fe-1, Nb-Ta 3.2 Packing In A 25 Kg Cardboard Package. 7 Argon Welding Rod D=2.4 X 1000 Mm Tigroid 316 L Type Or Analog 18% Cr - 8% Ni And 18% Cr - 10% Ni - 3% Mo Type Austenitic Stainless For Welding Steels Non-Insulated, Corrosive Continuous Chromium-Nickel-Molybdenum Welding Sticks. Austenitic Type (About 10% Iron [Disclaimer: The Above Text Is Machine Translated. For Accurate Information Kindly Refer The Original Document.] Tender Link : Https://Socar.Az/Mediafiles/Procurements/Satinalma-Elanlari/Az/25031-23-Elan_Qaynaq_Mftillri.Docx
